A low-expansion Fe--Ni based alloy for semi-tension masks with excellent creep properties consists of, in mass percentage, from 34 to 38% Ni, from 0.01 to 0.5% Mn, from 0.0003 to 0.0015% B, from 0.0010 to 0.0050% N, and the balance Fe and unavoidable impurities. The alloy further includes from 0.005 to 0.20% Si and from 0.005 to 0.030% Al. Among the unavoidable impurities, C, P and S are controlled to no more than 0.010%, no more than 0.015%, and no more than 0.010%, respectively. The alloy is subjected, at least once after hot rolling or after cold rolling, to annealing in a non-oxidizing atmosphere at between 650 and 750.degree. C. for from 30 minutes to less than 5 hours. The alloy is subjected to stress relief annealing after final cold rolling. A semi-tension mask using the alloy and a color picture tube using the semi-stretched-tension mask, are also provided.

Fe низк-raswireni4 -- сплав основанный ni для маск семи-napr4jeni4 с превосходными свойствами ползучести состоит, в массовом проценте, от ni от 34 до 38%, от от 0.01 до 0.5% марганца, от от 0.0003 до 0.0015% б, от от 0.0010 до 0.0050% н, и примеси fe баланса и неизбежных. Сплав более дальнейший вклюает от от 0.005 до 0.20% кремния и от от 0.005 до 0.030% al. Среди неизбежных примесей, ч, п и с проконтролированы до no more чем 0.010%, no more чем 0.015%, и no more чем 0.010%, соответственно. Сплав подвергается, по крайней мере раз после горячей завальцовки или после холодной завальцовки, к обжигать в нон-okisl44 атмосфере на между 650 и 750.degree. C на от 30 минут до меньш чем 5 часов. Сплав подвергается к отжигу сброса усилия после окончательной холодной завальцовки. Маска семи-napr4jeni4 использующ сплав и цвет изображают пробку использующ маску семи-протягивать-napr4jeni4, также обеспечены.