Improved monodisperse spheroidal particle latices of vinyl chloride polymers, e.g., having particle sizes ranging from 0.17 to 0.8 .mu.m or from 0.5 to 1.2 .mu.m, are produced by aqueous emulsion polymerization of vinyl chloride monomer, whether in a single stage or in two stages, in the absence of surface-active agent, in the presence of at least 0.2% by weight of at least one water-soluble alkali metal or ammonium persulfate initiator, and also in the presence of at least one water-soluble auxiliary compound that is a solvent for vinyl chloride, in such amount that the solubility of vinyl chloride in the aqueous phase at 25.degree. C. at atmospheric pressure is at least 1.5 g/l.

I lattici sferoidali migliorati della particella del monodisperse dei polimeri del cloruro di etile, per esempio, avendo dimensioni delle particelle variare da 0.17 a 0.8 mu.m o mu.m 0.5 - 1.2, sono prodotti tramite polimerizzazione acquosa dell'emulsione del monomero del cloruro di etile, se in una singola fase o in due fasi, in assenza dell'agente tensioattivo, in presenza almeno di 0.2% a peso di iniziatore solubile in acqua del persolfato dell'ammonio o almeno un del metallo alcalino ed anche in presenza almeno di un residuo ausiliario solubile in acqua che è un solvente per il cloruro di etile, in tale importo quel la solubilità del cloruro di etile nella fase acquosa a 25.degree. Il C. a pressione atmosferica è almeno 1.5 g/l.