In order to obtain sheets made of a nickel-based superalloy of type 718 having properties of superplasticity, the sheets are manufactured with a final cycle comprising the steps of: a) solution treatment at 1060.degree. C. for 15 minutes; b) precipitation at 730.degree. C. to 800.degree. C. for 1 to 2 hours; c) cold rolling at a ratio greater than 60%, and d) recrystallization at 900.degree. C. for 30 minutes. Superplastic deformation of such sheets is carried out at about 970.+-.10.degree. C. and under pressures inducing stresses between 45 and 60 MPa.

Afin d'obtenir des feuilles faites d'un superalloy nickel-basé du type 718 ayant des propriétés de superplasticity, les feuilles sont fabriquées avec un cycle final comportant les étapes de : a) traitement de solution à 1060.degree. C. pendant 15 minutes ; b) précipitation à 730.degree. C. à 800.degree. C. pendant 1 à 2 heures ; c) roulement à froid à un rapport 60% plus grand que, et d) recristallisation à 900.degree. C. pendant 30 minutes. La déformation de Superplastic de telles feuilles est effectuée à environ 970.+-.10.degree. C. et sous des pressions induisant des efforts entre 45 et 60 MPa.

 
Web www.patentalert.com

< (none)

< Robotic furniture texturing

> Enhancement of sleep with a tachykinin antagonist

> (none)

~ 00022