The present invention provides a thermosetting organic solvent type coating capable of forming a cured coating film having a TUKON hardness at 20.degree. C. of 15 or more and the minimum value of dynamic modulus E' at a frequency of 110 Hz in the temperature range of 150-200.degree. C., of 1.times.10.sup.9 dyn/cm or more. The cured film formed from the coating, as compared with the cured films formed from conventional organic solvent type coatings used as a top coat for automobile (e.g. an organic solvent type coating containing, as main components, a hydroxyl group-containing acrylic resin and a melamine resin, or a carboxylic-epoxy type coating), is at least equivalent in weatherabiIity, finish appearance, acid resistance, etc. and superior in stain resistance.

De onderhavige uitvinding verstrekt een thermosetting organisch oplosmiddeltype deklaag geschikt om een genezen het met een laag bedekken te vormen film die een hardheid TUKON heeft bij 20.degree. C. van 15 of meer en de minimumwaarde van dynamische modulus E ' bij een frequentie van 110 Herz in de temperatuurwaaier van 150-200.degree. C., van 1.times.10.sup.9 dyne/cm of meer. De genezen film die van de deklaag, vergeleken met de genezen films wordt gevormd die van conventionele organisch oplosmiddeltype deklagen worden gevormd die als hoogste laag voor auto (b.v. een organisch oplosmiddeltype deklaag die bevat worden gebruikt, als hoofdcomponenten, een hydroxyl groep-bevattende acrylhars en een melaminehars, of een carboxylic-epoxytypedeklaag), is minstens gelijkwaardig in weatherabiIity, beëindigt verschijning, zure weerstand, enz. en meerdere in vlekweerstand.