A layered structure manganese dioxide (MnO.sub.2) of which oxide lattices are in the pattern of pseudo-hexagonal close packing ( . . . AABB . . . ) and has hexagonal P6.sub.3 /mmc space group or orthorhombic Cmcm space group. The present invention also provides a process for producing said layered structure manganese dioxide (MnO.sub.2) which comprises heat treating a mixture of an alkali metal compound and a manganese compound at a high temperature. During the process, bismuth compounds or lead compounds may be added in order to stabilize the layered crystal structure of MnO.sub.2, or lithium compounds may be added in order to improve the reversibility of charge and discharge. The layered structure MnO.sub.2 is suitable for use as a cathode material in lithium rechargeable cells, since it does not transform into a spinel phase during charge and discharge cycling, thus having an excellent charging and discharging reversibility.

Un bioxyde posé de manganèse de structure (MnO.sub.2) dont l'oxyde treillage sont dans le modèle de l'emballage étroit pseudo-hexagonal (. . . AABB. . . ) et a le groupe hexagonal de l'espace de P6.sub.3 /mmc ou le groupe orthorhombic de l'espace Cmcm. La présente invention fournit également un processus pour produire le bioxyde posé de manganèse de structure (MnO.sub.2) qui comporte la chaleur traitant un mélange d'un composé alcalin composé et de manganèse à température élevée. Pendant le processus, des composés de bismuth ou les composés de plomb peuvent être ajoutés afin de stabiliser la structure en cristal posée de MnO.sub.2, ou des composés de lithium peuvent être ajoutés afin d'améliorer la réversibilité de la charge et de la décharge. La structure posée MnO.sub.2 convient pour l'usage comme matériel de cathode en cellules rechargeables de lithium, puisqu'elle ne transforme pas en phase à spinelle pendant la charge et ne décharge pas le cycle, de ce fait ayant une excellente réversibilité de remplissage et de décharge.