This invention provides a welding material for low chromium (Cr) ferritic heat-resisting steel having high toughness, wherein the chemical composition of welding metal comprises, in weight %, carbon (c) 0.04-0.1%, silicon (Si) 0.1-0.6%, manganese (Mn) 0.1-0.6%, phosphorus (P) 0.0005-0.03%, sulfur (S) 0.0005-0.015%, chromium (Cr) 1.75-2.5%, nickel (Ni) 0.01-0.8%, molybdenum (Mo) 0.05-1.5%, vanadium (V)0.01-0.5%, tungsten (W) 0.05-2%, niobium (Nb) 0.01-0.2%, tantalum (Ta) 0.01-0.5%, aluminum (Al) 0.003-0.05%, boron (B) 0.0001-0.01%, nitrogen (N) 0.003-0.03%, and the remainder comprises iron and inevitable impurities. The welding material satisfies the following formula: C+Cr/20+Mo/15+V/10+W/7+5B.ltoreq.0.8%. According to this invention, the welding material is suitable for welding low Cr ferritic heat-resisting steels having high strength such as those used in steam generators and heat exchangers of boilers, etc. which are exposed to high temperatures and high pressures, more particularly, at a high temperature of 500.degree. C. or more.

Esta invención proporciona un material de la soldadura para el acero heat-resisting ferritic bajo del cromo (cr) que tiene alta dureza, en donde la composición química del metal de la soldadura abarca, en el peso %, carbón (c) 0.04-0.1%, silicio (silicio) 0.1-0.6%, manganeso (manganeso) 0.1-0.6%, fósforo (p) 0.0005-0.03%, sulfuro (s) 0.0005-0.015%, cromo (cr) 1.75-2.5%, níquel (Ni) 0.01-0.8%, molibdeno (MES) 0.05-1.5%, vanadio (el V)0.01-0.5%, el tungsteno (w) 0.05-2%, el niobium (NOTA) 0.01-0.2%, el tantalio (TA) 0.01-0.5%, aluminio (al) 0.003-0.05%, el boro (b) 0.0001-0.01%, el nitrógeno (n) 0.003-0.03%, y el resto abarca el hierro e impurezas inevitables. El material de la soldadura satisface el fórmula siguiente: El C+Cr/20+Mo/15+V/10+W/7+5B.ltoreq.0.8%. Según esta invención, el material de la soldadura es conveniente para los aceros heat-resisting ferritic del cr bajo de la soldadura que tienen alta fuerza tal como ésos usados en generadores del vapor y cambiadores de calor de las calderas, de los etc. que se exponen a las altas temperaturas y a las altas presiones, más particularmente, en una temperatura alta de 500.degree. C. o más.

 
Web www.patentalert.com

< (none)

< Method for customizing dermatological foundation products

> Silicon carbide reinforced reaction bonded silicon carbide composite

> (none)

~ 00001